ASTM B167 Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, N06045, and N06696), Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617), and Nickel-Iron-Chromium-Tungsten Alloy (UNS N06674) Seamless Pipe and Tube
| Standard | ASTM B167 |
| Material | UNS N06690(Inconel 690) |
| Equivalent Materials | 2.4642, Inconel 690, 0Cr30Ni60Fe10, NiCr29Fe |
| Related Products | ASTM B167, Nickel-Chromium-Iron Alloys Tube, Nickel-Chromium-Cobalt-Molybdenum Alloy Tube, Nickel-Iron-Chromium-Tungsten Alloy Tube, Seamless Pipe Seamless Tube, UNS N06025, UNS N06045, UNS N06600, UNS N06601, UNS N06603, UNS N06617, UNS N06674, UNS N06690, UNS N06693, UNS N06696 |
Chemical Composition of ASTM B167 UNS N06690 Nickel And Nickel Alloy Tubes
| Ni % | Cr % | Fe% | Mn % | C % | Cu % | Si % | S % |
| 58.0 min | 27.0-31.0 | 7.00-11.0 | 0.50 max | 0.05 max | 0.50 max | 0.50 max | 0.015 max |
Mechanical Properties of ASTM B167 UNS N06690 Nickel And Nickel Alloy Tubes
| Tensile Strength, Mpa | Yield Strength, MPa | Elongation, % | Outside Diameter, mm | |
| 586 min | 205 min | 35 min | OD<=127 | Hot-worked or Hot-worked Annealed |
| 515 min | 170 min | 35 min | OD>=127 | |
| 586 min | 240 min | 30 min | OD<=127 | Cold-worked Annealed |
| 586 min | 205 min | 35 min | OD>=127 |